CAS No.: | 13674-84-5 |
---|---|
Formula: | C9h18po4cl3 |
EINECS: | 237-158-7 |
Source: | Organic Acids |
Appearance: | Oily Liquid |
Grade Standard: | Industrial Grade |
Samples: |
---|
Suppliers with verified business licenses
Appearance | Colorless or slightly yellow transparent liquid |
Viscosity(25ºC,mPa.s) | 65.0-70.0 |
Density( dºC) | 1.27-1.31 |
Acid value (mgKOH/g) | ≤0.10 |
Water(%) | ≤0.10 |
Color(Pt-Co) | ≤50 |
Refractivity( n) | 1.460~1.469 |
P CONTENT(%wt) | 9.30-9.45 |
CL CONTENT(%wt) | 32.10-32.50 |
Products merits
1) The final products using this flame retardant will be no frost and whity.
2) Low additive so save the cost. It can be added directly in LDPE, reduce the process stage so save cost.
3) It meet the standard RoHS, no powder and no pollution.
4) Good heat stability and suitable for process in high temperature (≥200°C).
5) The density for final products is ≤1.0, the density for Br flame retardant is about 1.3.
6) Good physical performance and stay the same physical performance as resin (consistency with resin).
Application
Flame retardant in PE;
Flame retardant in new PP, in recycling PP, in transparent PP; in PP with glass fiber reinforced;
Flame retardant in PVC;
Flame retardant in PC; in transparent PC;
Flame retardant in PA6; PA66; PA6, PA66 with glass fiber reinforced;
TCPP is mainly used for the production of hard and soft polyurethane foam, PVC, ring chloride resin, acrylic resin, polystyrene, cellulose acetate, ethyl cellulose, phenolic resin, polyvinyl acetate, polyvinyl chloride, rubber and coating as flame retardant. Particularly recommend it to use in rigid polyurethane foam compounds polyurethane foam, unsaturated polyester resin and phenolic plastics because of its good thermal conductivity and hydrolysis stability. It is also used in the production raw materials of BDP. At low temperature, it present low viscosity. Often used with antimonous oxide to improve the flame retardant efficiency. Please ask the sales staff for detailed purposes and usage.
Usage
1) Used as flame retardant ,used in PU foam etc.
2) TCPP is mainly applied to soft (hard) PU foam, epoxy resin, polystyrene, acrylic acid,
cellulose acetate, ethyl cellulose resin, bakelite, polyvinyl acetate, and foam gap filler, especially for thermal conduction of hard PU foam and stability of hydrolyze, as well as for the synthetic PU foam and saturation resin and bakelite with low viscosity under low temperature.
3) Applying as Flame Retardant in the production of acetate fiber, polyvinyl-chloride, PU foams, EVA, phenolics materials. Except the flame retarding, it can also promote the moisture resisting, low temperature resisting, the capability of antistatic and the softness of the materials.